Shenzhen Tunsing Plastic Products Co., Ltd.
ts02@tunsing.com.cn
86-755-8996-0062
Product Details
Place of Origin: China
Brand Name: /
Certification: ISO, ROHS, REACH, Oeko-Tex
Model Number: DS001TS
Payment & Shipping Terms
Minimum Order Quantity: Two rolls in a carton if in stock.
Price: USD60.00-65.00/roll
Packaging Details: 1-2 rolls in one box，each with black PE bag and Plugs.
Delivery Time: 3-15 work days after payment
Payment Terms: L/C,T/T,PayPal
Supply Ability: 500 rolls per week
|
Colour:
|
Milky White Translucent
|
Thickness Range:
|
0.025mm-0.30mm
|
Width Range:
|
5mm-1580mm
|
Proportion:
|
1.15±0.02g/cm³
|
Melt Flow Index:
|
32±15g/10min（ASTM D1238-04）
|
Melting Range:
|
80-105℃ (Tunsing DSC 214)
|
TG Temperature:
|
0±5℃ (GB/T19466.2-2004)
|
Activation Temperature:
|
116-150℃ (Tunsing)
|
|
Colour:
|
Milky White Translucent
|
|
Thickness Range:
|
0.025mm-0.30mm
|
|
Width Range:
|
5mm-1580mm
|
|
Proportion:
|
1.15±0.02g/cm³
|
|
Melt Flow Index:
|
32±15g/10min（ASTM D1238-04）
|
|
Melting Range:
|
80-105℃ (Tunsing DSC 214)
|
|
TG Temperature:
|
0±5℃ (GB/T19466.2-2004)
|
|
Activation Temperature:
|
116-150℃ (Tunsing)
|
This product is a thermoplastic film hot melt adhesive with the release paper, can be repeatedly heated and plasticized for bonding.This kind of hot melt adhesive has excellent adhesion to textile products, PVC, PC.This product is resistant to dry cleaning and 40℃ washing.
Copolyester
| Color | Milky White Translucent |
| Proportion | 1.15±0.02g/cm³ |
| Melt Flow Index | 32±15g/10min(ASTM D1238-04) |
| Melting Range | 80-105℃ (Tunsing DSC 214) |
| Width Range | 5mm-1580mm |
| TG Temperature | 0±5℃ (GB/T19466.2-2004) |
| First Lamination | Second Implanting | ||
| Mechanical Mold Temperature | 130℃-140℃ | Mechanical Mold Temperature | 130℃-180℃ |
| Time | 5-15 seconds | Packing Time | 8-25 seconds |
| Pressure | 0.3-0.6mpa | Pressure | 0.3-0.6mpa |
DS001TS is applied to clothing, footwear, accessories, reflective materials, handbags, bags, embroidery, crafts bonding. product aesthetics, functionality, and durability.