|Melt Flow Index:||5±3g/10mins （ASTM D1238-04）||Hardness:||81±3（Shore A）|
|Melting Range:||110-140℃ (Tunsing DSC 214)||Activation Temperature:||125-174℃ （Tunsing）|
|Conventional Thickness:||0.15mm||Conventional Width:||1380mm|
|Finished Product:||1380mm*100yards/roll||Conventional Length:||100 Yards|
1380mm TPU Hot Melt Adhesive Film,
0.15mm TPU Hot Melt Adhesive Film,
1380mm Transparent Polyurethane
Transparent Polyurethane Double Sided TPU Hot Melt Adhesive Film for PU Materials
This product is a thermoplastic hot-melt adhesive film, which is supported by release paper and can be repeatedly heated and plasticized. This hot melt adhesive has excellent adhesion to textiles, TPU, PVC, and has good feel and resilience, and excellent cold resistance.
|Colour||Transparent||Release Protection||Glassine Release Paper|
|Melt Flow Index||5±3g/10mins (ASTM D1238-04)||Conventional Thickness||0.15mm|
|Hardness||81±3 (Shore A)||Conventional Width||1380mm|
|Melting Range||110-140℃ (Tunsing DSC 214)||Conventional Length||100 yards|
|Activation Temperature||125-174℃ (Tunsing)||Finished Product||1380mm*100yards/roll|
Recommended Bonding Conditions:
|First Lamination||Second Implanting|
|Mechanical Mold Temperature||150℃-170℃||Mechanical Mold Temperature||160℃-200℃|
|Time||5-15 seconds||Time||8-25 seconds|
1. Bonding temperature and pressure and time relate to the bonding strength of the film to the material. The bonding temperature must be close to the temperature set by the machine, the pressure must be uniform, and the mold and press rolls must be flat.
2. The bonding conditions used will vary between machines and materials. The conditions indicated here are only basic. The most ideal bonding conditions should be established by manufacturing for the specific application.
Note: The seller hereby declares that Tunsing will refuse to accept the assurance of the components of the manufacturing process.Tunsing firmly believes that the information content is reliable. However, the claims for possible problems will not be guaranteed for the components of a particular process. Before use, the manufacturer must determine the suitability of the product for the items to be used. The user must bear the risks and possible problems in the various manufacturing stages of testing and use. The Seller and the manufacturer shall not be liable for any direct injury, loss, damage or misuse.
The Applications of Polyurethane Double Sided TPU Hot Melt Adhesive Film
DS8501 is used in the bonding of clothing, embroidery, footwear, luggage, handbags, toys, hats, sports materials.
Packing Details:100Y/roll , 1rolls/ctn
Delivery Time:Shipped in 3-5 days after payment
tpu hot melt adhesive film
We are based in Guangdong, China, start from 2007,sell to Domestic Market(50.00%),South America(12.00%),South Asia(12.00%),North America(6.00%),Southeast Asia(5.00%),Africa(5.00%),Western Europe(2.00%),Southern Europe(2.00%),Eastern Europe(00.00%),Oceania(00.00%),Mid East(00.00%),Eastern Asia(00.00%),Central America(00.00%),Northern Europe(00.00%). There are total about 51-100 people in our office.
Always a pre-production sample before mass production;
Always final Inspection before shipment;
Hot Melt Adhesive Film,Hot Melt Adhesive Powder,Hot Melt Adhesive Web Film,Hot Melt Adhesive Granule,Heat Seam Sealing Tape
1.ISO9001,ROHS,REACH & Oeko-Tex Standard 100 certification 2.More than fourteen years experience 3.Strict quality control 4.ERP system
Accepted Delivery Terms: FOB,CFR,CIF,EXW,Express Delivery；
Accepted Payment Currency:USD,HKD,CNY;
Accepted Payment Type: T/T,L/C,D/P D/A,Credit Card,PayPal,Western Union,Cash;
Contact Person: Cynthia Liang
Tel: 86 18126266192